Co-extrusion conductive gasket
Co extruded conductive silicone rubber material is composed of conductive rubber and non-conductive silica gel. It has excellent shielding efficiency, good water / gas sealing performance and corrosion resistance.
Co-extrusion conductive gasket
Product description
Co extruded conductive silicone rubber material is composed of conductive rubber and non-conductive silica gel. It has excellent shielding efficiency, good water / gas sealing performance and corrosion resistance. The material can maintain long-term stability over a wide temperature range. Conductive silica gel mainly contains Ag / g, Ag / Al and Ni / C materials, which can meet the use requirements of customers through a variety of cross-section shapes.
Coextrusion material can save more space and cost, and achieve good air tightness and shielding effect at the same time. Non conductive rubber can provide excellent mechanical properties and reliability, and the conductive part can provide excellent shielding effect. And it can also provide more excellent compressibility during installation.
Product features
▪ Excellent electromagnetic shielding efficiency
▪ Good mechanical properties
▪ Excellent compression deformation performance provides better sealing effect
▪ Wide operating temperature range
▪ Excellent cost and space saving
Typical application
▪ Communication equipment
▪ Aerospace
▪ Sealing of outdoor equipment
▪ outdoor
▪ Automotive electronics
Technical parameter
Standard section shape*
*It is only a typical shape example, and more shapes and sizes can be customized.
Product description
Co extruded conductive silicone rubber material is composed of conductive rubber and non-conductive silica gel. It has excellent shielding efficiency, good water / gas sealing performance and corrosion resistance. The material can maintain long-term stability over a wide temperature range. Conductive silica gel mainly contains Ag / g, Ag / Al and Ni / C materials, which can meet the use requirements of customers through a variety of cross-section shapes.
Coextrusion material can save more space and cost, and achieve good air tightness and shielding effect at the same time. Non conductive rubber can provide excellent mechanical properties and reliability, and the conductive part can provide excellent shielding effect. And it can also provide more excellent compressibility during installation.
Product features
▪ Excellent electromagnetic shielding efficiency
▪ Good mechanical properties
▪ Excellent compression deformation performance provides better sealing effect
▪ Wide operating temperature range
▪ Excellent cost and space saving
Typical application
▪ Communication equipment
▪ Aerospace
▪ Sealing of outdoor equipment
▪ outdoor
▪ Automotive electronics
Technical parameter
| performance | standard | Conductive filler type | |||
| Ag/G | Ag/Cu | Ag/Al | Ni/C | ||
| Silicone color / conductive side color | / | Grey / yellow | Orange / yellow | Orange / yellow | Blue / Black |
| Silica gel density(g/cm3), ±0.25 | ASTM D792 | 1.2 | 1.2 | 1.1 | 1.2 |
| Conductive side density(g/cm3), ±0.25 | ASTM D792 | 2.0 | 2.2 | 2.1 | 2.1 |
| Silicone hardness,Shore A, ±5 | ASTM D 2240 | 50 | 55 | 50 | 60 |
| Hardness of conductive side,Shore A, ±5 | ASTM D 2240 | 65 | 80 | 65 | 70 |
| Tensile strength of silica gel, MPa, Min | ASTM D412 | 2.5 | 4.5 | 4.0 | 3.5 |
| Tensile strength of conductive side,MPa, Min | ASTM D412 | 1.5 | 1.0 | 1.0 | 1.5 |
| Elongation at break on silica gel side,%, Min | ASTM D412 | 200 | 300 | 300 | 150 |
| Elongation at break on conductive side,%, Min | ASTM D412 | 150 | 150 | 150 | 230 |
| Tear strength of silica gel side,kN/m, Min | ASTM D412 | 11 | 11 | 11 | 9 |
| Volume resistivity,Ω•cm | MIL-DTL-8352 C | 0.01 | 0.004 | 0.008 | 0.1 |
| Shielding effectiveness, dB | |||||
| 200kHz（H-Field） | MIL-DTL-83528 C | 50 | 60 | 60 | 50 |
| 100MHz（E-Field） | MIL-DTL-83528 C | 100 | 115 | 115 | 100 |
| 500MHz（E-Field） | MIL-DTL-83528 C | 100 | 110 | 110 | 100 |
| 1GHz（Plane Wave） | MIL-DTL-83528 C | 90 | 110 | 105 | 90 |
| 2GHz（Plane Wave） | MIL-DTL-83528 C | 90 | 110 | 105 | 90 |
| 10GHz（Plane Wave） | MIL-DTL-83528 C | 80 | 110 | 100 | 90 |
| Operating temperature,℃ | ASTM D1329 | -55~200 | -55~200 | -55~200 | -55~200 |
| Permanent compression deformation,% (100℃*70h*30%), Max | ASTM D395 | 10 | 10 | 10 | 17 |
| Flame retardant grade | UL 94 | HB | HB | HB | HB |
| workmanship | / | Co-extrusion | Co-extrusion | Co-extrusion | Co-extrusion |
Standard section shape*
 Conductive side Non conducting side |
 Conductive side Non conducting side |
 Conductive side Non conducting side |
 Conductive side Non conducting side |